STONE | BUILDING | PERFORMANCE | WORLDWIDE
“Heraclea White – “strong and distinguished white”
Diagonal straight veining character of this white marble shows attitude and climaxes the luxurious aspect of your project and personality.
Imposing white background comes to contrast the rainfall-like dark greyish veining of this marble, creating a calm symmetry, that will leave a unique stigma wherever it is placed.
Being quarried in EAGLE’s own quarry, Heraclea White can become the protagonist of every high scale project, where harmonic claddings and floorings will highlight the quality, endurance and luxury this eternal construction material provides.
‘’Quality is not an act, it is a habit’’
-Aristotle
Eagle is a highly experienced end-to-end company in the marble industry that offers complete and customized solutions tailored to its clients’ needs.
Eagle starts its journey from the quarries that produce our excellent quality marbles, ‘’flies’’ through a whole production process and treatment at its high-end facilities, using state-of-art machinery, to finally end up fulfilling its purpose· to adorn your place exactly the way you imagined it.
Our high level of expertise, know how and high-tech machines, allow us to have absolutely no limit to our productive capabilities. All above, combined with the special attention we give to the unique needs of our each customer, is the main reason why more and more customers are choosing Eagle every day for their projects. What about you?
In Eagle we like to think differently. That’s why our whole philosophy revolves around a single ideology· ‘’No’’ is not an option.
Our customers find only solutions that serve and care for their needs. What can be challenging for some, for Eagle’s team is self- evident. The development of relationships of trust with the customers, the quality and the efficiency of our work, is the driving force of our journey over the years. Our strong will to adapt ourselves to the customer’s needs rather than vice versa, seriously and responsibly, is the reason why we stand out from the competition.
Heraclea White
Apparent density (EN 1936) kg/m³ |
: |
2770 Kg/m3 |
Absorption Coefficiet
|
: |
0.23 wt% |
Compression Strength
|
: |
990 Kg/cm2 |
Modulus of Rupture |
: |
132 Kg/cm2 |
Abrasion Resistance (after 1000 m) |
: |
6.58 mm |
Microhardness Knoop |
: |
321.6 Kg/mm2 |
Calcite (%) |
: |
8 |
Dolomite (%) |
: |
90 |
Quartz (%) |
: |
2 |
SIVEC White Marble®
Apparent density (EN 1936) kg/m³ |
: |
2770 Kg/m3 |
Absorption Coefficiet
|
: |
0.23 wt% |
Compression Strength
|
: |
990 Kg/cm2 |
Modulus of Rupture |
: |
132 Kg/cm2 |
Abrasion Resistance (after 1000 m) |
: |
6.58 mm |
Microhardness Knoop |
: |
321.6 Kg/mm2 |
Calcite (%) |
: |
8 |
Dolomite (%) |
: |
90 |
Quartz (%) |
: |
2 |
THASSOS Snow White Marble
Apparent density (EN 1936) kg/m³ |
: |
2770 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0,7 |
Water absorption at atmospheric pressure (ΕΝ 13755) % wt. |
: |
0,2 |
Uniaxial compressive strength (ΕΝ 1926) MPa |
: |
164 |
Flexural strength under concentrated load (ΕΝ 12372) Mpa |
: |
18,5 |
Breaking load at dowel hole (ΕΝ 13364) N |
: |
2250 |
Abrasion resistance (ΕΝ 14157 - Β) mm³ |
: |
24313 |
Rupture energy (ΕΝ 14158) Joule |
: |
4 |
Flexural strength under concentrated load (ΕΝ 12372) after 48 frost resistance cycles MPa |
: |
15,7 |
VOLAKAS Marble
Apparent density (EN 1936) kg/m³ |
: |
2825 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0,54 |
Compressive Strength - Dry Condition |
: |
138.6 N/mm2 |
Compressive Strength - Wet Condition |
: |
145.9 N/mm2 |
Compressive Strength - After Freeze |
: |
102.6 N/mm2 |
Flexural Strength - Dry Condition |
: |
9.90 MPa |
Flexural Strength - Wet Condition |
: |
10.76 MPa |
Modulus of Elasticity |
: |
35 GPa |
Abrasion Resistance |
: |
2.20 mm |
Impact Strength |
59 cm |
PRINOS Marble
Apparent density (EN 1936) kg/m³ |
: |
2840 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0,4 |
Water Absorption |
: |
0.1% wt |
Compressive Strength |
: |
151.6 MPa |
Flexural Strength |
: |
15.9 MPa |
Frost Resistance |
: |
145.1 MPa |
Abrasion Resistance |
: |
21.287 mm3 |
Rupture Energy |
: |
3 J |
PRINOS LIGHT Marble
Apparent density (EN 1936) kg/m³ |
: |
2840 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0,4 |
Water Absorption |
: |
0.1% wt |
Compressive Strength |
: |
151.6 MPa |
Flexural Strength |
: |
15.9 MPa |
Frost Resistance |
: |
145.1 MPa |
Abrasion Resistance |
: |
21.287 mm3 |
Rupture Energy |
: |
3 J |
SILVERSTREAM PRINOS Marble
Apparent density (EN 1936) kg/m³ |
: |
2840 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0,4 |
Water Absorption |
: |
0.1% wt |
Compressive Strength |
: |
151.6 MPa |
Flexural Strength |
: |
15.9 MPa |
Frost Resistance |
: |
145.1 MPa |
Abrasion Resistance |
: |
21.287 mm3 |
Rupture Energy |
: |
3 J |
BIANCO VENUS Marble
Apparent density (EN 1936) kg/m³ |
: |
2820 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
1.5 |
Water Absorption |
: |
0.6% wt |
Water Absorption Due to Capillarity |
: |
5.755 |
Flexural Strength |
: |
3.4 MPa |
Breaking Load at Dowel Hole |
: |
700 N |
Compressive Strength |
: |
2.9 MPa |
BIANCO VENATINO Marble
Apparent density (EN 1936) kg/m³ |
: |
2830 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
1.1 |
Water Absorption |
: |
0.3% wt |
Flexural Strength |
: |
6.3 MPa |
Breaking Load at Dowel Hole |
: |
1350 N |
Compressive Strength |
: |
2.9 MPa |
BUTTERFLY Marble
Apparent Specific Gravity (EN 1936) kg/m³ |
: |
2825 Kg/m3 |
Open porosity (EN 1936) % vol. |
: |
0.54 |
Water Absorption |
: |
0.19% wt |
Compressive Strength - Dry Condition |
: |
138.6 N/mm2 |
Compressive Strength - Wet Condition |
: |
145.9 N/mm2 |
Compressive Strength After Freeze / Thaw Cycles |
: |
102.6 N/mm2 |
Flexural Strength - Dry Condition |
: |
9.90 MPa |
Flexural Strength - Wet Condition |
: |
10.76 MPa |
Modulus of Elasticity |
: |
35 GPa |
Abrasion Resistance |
: |
2.20 mm |
Impact Strength |
: |
59 cm |
DAMASTA Marble
Apparent density (EN 1936) kg/m³ |
: |
2.770 Kg/m3 |
Water absorption at atmospheric pressure (ΕΝ 13755) % wt. |
: |
0,23 |
Compressive Strength (DIN 52105 / ASATM C-170 / EN 1926): |
: |
990 Kg/cm² |
Friction Wear (DIN 52108): |
: |
6,50 mm |
CREMA MARFIL Marble
Bulk Specific Gravity |
: |
2.660 Kg/m3 |
Water absorption at atmospheric pressure (ΕΝ 13755) % wt. |
: |
0,27 |
Modulus of Rupture - Dry |
: |
10.3 MPa / 1490 psi |
Modulus of Rupture - Wet |
: |
10.2 MPa / 1480 psi |
Compressive Strength - Dry | 208 MPa / 30100 psi | |
Compressive Strength - Wet | 184 MPa / 26700 psi | |
Abrasion Resistance of Stone Subjected to Foot Traffic | 4.1 | |
Flexural Strength - Dry | 8 MPa / 1160 psi | |
Flexural Strength - Wet | 7.9 MPa / 1140 psi |
The passion we have for our work at Eagle, appears in everything that makes up this company. The projects and the quality of our work may speak for itself, but to successfully complete a project it first goes through an entire process in our facilities, for which we have every reason to be proud. Eagle’s main facilities, covering a total area of 70.000 square meters, are thought to be a real gem for the marble industry
Being able to reflect on such a remarkable natural product as the marbles, anything that an architect or an artist can imagine, is itself something that excites us and makes us work on every project with the same commitment for a flawless outcome. At Eagle, the passion, the dedication and the ability to be able to bring to life every thought you have for your project are making the perfect combination that allows us to stand out from our competition. To explore all possibilities that natural stone has to offer, you need the right partner with mindset and capacity to support your inspiration without limitations. Contact us to find solutions and ideas tailored to your own needs.